Butadiene Rubber

The BR polymer family contains polybutadiene rubbers which are divided into different categories according to their polymerization process and application field.

Filter by:
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 38 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 90 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 5,0 Internal Method
Lithium BR
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 68 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 250 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 4,5 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 53 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 165 mPa.s Internal Method
Cis 1,4 Content 36 %
Color < 7,5 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 54 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 163 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 4,5 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 60 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 44 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 4,5 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 38 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 90 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 5,0 Internal Method
Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 68 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 250 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 4,5 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 54 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 163 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 5,0 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 54 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 163 mPa.s Internal Method
Cis 1,4 Content 38 %
Color < 5,0 Internal Method
Lithium BR, Plastic Modification
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 70 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Solution Viscosity 250 mPa.s Internal Method
Cis 1,4 Content 36 %
Color < 10,0 Internal Method